PVC250 is a rigid PVC film with gloss/gloss surface. PVC250 has been engineered for use in the printing industry. It has excellent printing characteristics as well as customized impact properties. Typical application of this material are for greeting cards, advertisement cards, large placards and regular membership cards. Special requirement options of PVC250 include (but not limited to).
Coron a treatment (T) -40 above of dyne level for a least one month since production Transparent and opaque.
Coron a treatment (T) -40 above of dyne level for a least one month since production Transparent and opaque.
Unit of Measure
Typical Property Values
Roll Thickness |
N/A 5.0 to 10.0 mil |
Roll and Sheet Thickness |
N/A 10.0 to 30.0 mil |
Film Thickness Tolerance (±) |
N/A 5 %7 % |
Roll Width Tolerance (±) |
N/A 0.1116 in |
Square Cut Width Tolerance (±) |
N/A 0.1132 in |
Color |
N/A Various |
Gloss Value Angle |
N/A 60 º |
Gloss Value (Lightly Tinted Transparent) at 60 Degree Angle |
N/A 135 |
Gloss Value Tolerance (±) (Lightly Tinted Transparent) at 60 Degree Angle |
N/A 10 |
Gloss Value (Deeply Tinted Transparent) at 60 Degree Angle |
N/A 100 |
Gloss Value Tolerance (±) (Deeply Tinted Transparent) at 60 Degree Angle |
N/A 25 |
Gloss Value (Opaque) at 60 Degree Angle |
N/A 90 |
Gloss Value Tolerance (±) (Opaque) at 60 Degree Angle |
N/A 15 |
Test Method for Gloss Value |
N/A ASTM-D523 |
Specific Gravity (Transparent) |
N/A 1.34 |
Specific Gravity Tolerance (±) (Transparent) |
N/A 0.02 |
Specific Gravity (Opaque) |
N/A 1.40 |
Specific Gravity Tolerance (±) (Opaque) |
N/A 0.04 |
Test Method for Specific Gravity |
N/A ASTM-0792 |
Minimum Tensile Strength |
N/A 6000 psi |
Test Method for Minimum Tensile Strength |
N/A ASTM-D638 |
Minimum Elongation |
N/A 100 %70 %20 Mil↓ 20.1 Mil↑ |
Test Method for Minimum Elongation |
N/A ASTM-D638 |
Heat Distortion Temperature at 264 Pound Per Square Inch (psi) Pressure |
N/A 152 ºF |
Heat Distortion Temperature Tolerance (± ) at 264 Pound Per Square Inch (psi) Pressure |
N/A 5 ºF |
Test Method for Heat Distortion Temperature |
N/A ASTM-D648 |
Vicat Softening Temperature |
N/A 89 ºC |
Vicat Softening Temperature Tolerance (± ) |
N/A 2 ºC |
Test Method for Vicat Softening Temperature |
N/A ASTM-D1525 |
Minimum Dyne Level |
N/A 32 |
Test Method for Dyne Level |
N/A ASTM-D2578 |
Customized Impact Strengths |
N/A Extra High (EXX) High (HXX) Very High (VXX) |
Cold-Break Temperature for High Impact Strength (HXX) |
N/A -4 ºF |
Cold-Break Temperature for Very High Impact Strength (VXX) |
N/A -22 ºF |
Cold-Break Temperature for Extra High Impact Strength (EXX) |
N/A -31 ºF |
Test Method for Cold-Break Temperature |
N/A ASTM-D1790 |
Ultraviolet (UV) Resistance |
N/A Only when Requested |
Test Method for Ultraviolet (UV) Resistance |
N/A ASTM-G-53 |
Note for Ultraviolet (UV) Resistance |
N/A This test result only suggests if there is an improvement in the UV resistance, not the actual durability for outdoor or indoor use. |
Note for Typical Values |
N/A
Customized formulas for special requirements. For dimensions and/or physical properties different from what is listed above or special requirements including weatherability, etc., contact the vendor for the agreement on the specifications. |